VORIDIAN Polyethylene 808A Product Data Sheet
Propertya	Testb Method	Typical Value, Unitsc
Melt Index (Condition 190°C/2.16 kg)	D 1238	7 g/10 min
Density	D 4883	917  (0.917  )
Vicat Softening Temperature	D 1525	88°C (190°F)
Brittleness Temperature	D 746	<-73°C (<-99°F)
Tensile Stress @ Yield 500 mm/min (20 in./min)	D 638 Type IV Specimen	10 MPa (1500 psi)
Tensile Stress @ Break 500 mm/min (20 in./min)	D 638 Type IV Specimen	10 MPa (1500 psi)
Elongation @ Break 500 mm/min (20 in./min)	D 638 Type IV Specimen	400%
Flexural Modulus (2% Secant) 12.7 mm/min (0.5 in./min)	D 790	207 MPa (30000 psi)
aUnless noted otherwise, all tests are run at 23oC (73oF) and 50% relative humidity. bUnless noted otherwise, the test method is ASTM. cUnits are in SI or US customary units.
Applications VORIDIAN low density polyethylene 808A is a general-purpose formulation used for injection molding and general-purpose extrusion. General Where required, specimens are compression molded according to ASTM D1928. Comments Properties reported here are typical of average lots. Voridian makes no representation that the material in any particular shipment will conform exactly to the values given.
Neither Voridian nor its marketing affiliates shall be responsible for the use of this information, or of any product, method, or apparatus mentioned, and you must make your own determination of its suitability and completeness for your own use, for the protection of the environment, and for the health and safety of your employees and purchasers of your products. No warranty is made of the merchantability of fitness of any product, and nothing herein waives any of the Seller's conditions of sale.