MXSITE Advanced Linear Technology III LC78096-X
Product Data Sheet
| Propertya |
Testb Method |
Typical Value, Unitsc |
 |
||
|
||
| Resin Properties | ||
|
||
| Melt Index (Condition 190°C/2.16kg) | D 1238 | 1.1 g/10 min |
|
||
| Density | D 4883 | 913 kg/m3 (0.913 g/cm3) |
|
||
|
||
| Film Properties | ||
|
||
| Haze | D 1003 | 4.0% |
|
||
| Gloss @ 45° | D 2457 | 80 |
|
||
| Dart Impact | D 1709A | 400 g |
|
||
| Peel Cling, Aged 2 Weeks | ||
| 0% | D 5458 | 320 g |
| 200% | D 5458 | 210 g |
|
||
| Elmendorf Tear Resistance | ||
| M.D. | D 1922 | 400 gf |
| T.D. | D 1922 | 600 gf |
|
||
| Tensile Strength @ Break | ||
| M.D. | D 882 | 51 MPa (7400 psi) |
| T.D. | D 882 | 40 MPa (5800 psi) |
|
||
| Tensile Strength @ Yield | ||
| M.D. | D 882 | 14 MPa (2000 psi) |
| T.D. | D 882 | 12 MPa (1800 psi) |
|
||
| Elongation @ Break | ||
| M.D. | D 882 | 450% |
| T.D. | D 882 | 720% |
|
||
| Tensile Modulus, 1% Secant | ||
| M.D. | D 882 | 207 MPa (30000 psi) |
| T.D. | D 882 | 227 MPa (33000 psi) |
|
||
|
||
|
a Unless noted otherwise, all tests are run at 23oC (73oF) and 50% relative humidity. b Unless noted otherwise, the test method is ASTM. c Units are in SI or US customary units. |
||
|
|||
|
Conditions |
|||
| 50/50 blend of MXSITE LC78096-X and EASTMAN HIFOR LT24004-F, 0.7 mil (0.018 mm), 2.4:1 blow-up ratio and 4.7 lb/hr/inch die output. | |||
|
|
|||
|
Comments |
|||
| Properties reported here are typical of average lots. Eastman makes no representation that the material in any particular shipment will conform exactly to the values given. | |||
|
|
|||
|
Applications |
|||
| Eastman MXSITE LC78096-X polyethylene is designed for blown stretch cling film with quiet unwind. For monolayer film, it is recommended that it be blended with standard blown film LLDPE resins at approximately 50% of the entire film composition. Blended at these compositions, LC78096-X provides a substantial cling force in both a stretched and unstretched condition. For the skin layers of multilayer film, it is recommended that it be used at 100% in each of the skin layers. Each skin layer should be approximately 10-15% of the entire thickness. It is designed for high performance applications where low gel content and substantial cling are needed. | |||
|
|
|||
|
||
 |
||
|
Neither Eastman Chemical Company nor its marketing affiliates shall be
responsible for the use of this information, or of any product, method,
or apparatus mentioned, and you must make your own determination of its
suitability and completeness for your own use, for the protection of the
environment, and for the health and safety of your employees and purchasers
of your products. No warranty is made of the merchantability of fitness
of any product, and nothing herein waives any of the Seller's conditions of sale. |
||
| 4/11/00 8:53:58 AM | ||