MXSTEN POLYMER CM27051-F,
NATURAL EXTRA-LOW-DENSITY-POLYETHYLENE
Preliminary Data Sheet
| Propertya |
Testb Method |
Value, Unitsc |
 |
||
|
||
| Resin Properties | ||
|
||
| Melt Index (Condition 190°C/2.16kg) | D 1238 | 0.5 g/10 min |
|
||
| Density | D 4883 | 906 kg/m3 (0.906 g/cm3) |
|
||
|
||
| Film Properties | ||
|
||
| Thickness of Film Tested | 1.0 mils | |
|
||
| Haze | D 1003 | 15% |
|
||
| Gloss @ 45° | D 2457 | 50 |
|
||
| Dart Impact | D 1709A | >2000 g |
|
||
| Seal Initiation Temperature | Eastman | 80°C (175°F) |
|
||
| Elmendorf Tear Resistance | ||
| M.D. | D 1922 | 500 gf |
| T.D. | D 1922 | 600 gf |
|
||
| Tensile Strength @ Break | ||
| M.D. | D 882 | 68 MPa (9900 psi) |
| T.D. | D 882 | 55 MPa (8000 psi) |
|
||
| Tensile Strength @ Yieldd T.D. | D 882 | 14 MPa (2000 psi) |
|
||
| Elongation @ Break | ||
| M.D. | D 882 | 650% |
| T.D. | D 882 | 850% |
|
||
| Tensile Modulus, 1% Secant | ||
| M.D. | D 882 | 145 MPa (21000 psi) |
| T.D. | D 882 | 158 MPa (23000 psi) |
|
||
|
||
|
a Unless noted otherwise, all tests are run at 23oC (73oF) and 50% relative humidity. b Unless noted otherwise, the test method is ASTM. c Units are in SI or US customary units. d M.D. - DNY |
||
|
|||
|
Conditions |
|||
| Extrusion conditions used to produce 1 mil (0.025 mm) film include a 2.4:1 blow-up ratio and 4.7 lb/hr/inch die output. Density results are on Base Resin. | |||
|
|
|||
|
Comments |
|||
| Properties reported here are based on limited testing. Eastman makes no representation that the material in any particular shipment will conform exactly to the values given. | |||
|
|
|||
|
Applications |
|||
| MXSTEN CM27051-F is an extra low density polyethylene containing no slip, high antiblock and high processing aid. It is designed for blown film applications and is well suited for hygienic films and industrial packaging applications. CM27051-F works well as an enhancer in applications which require low temperature sealing, soft product feel and good lot-to-lot consistency. Films produced using CM27051-F exhibit superior, balanced tear resistance as well as low imperfections. | |||
|
|
|||
|
||
 |
||
|
Neither Eastman Chemical Company nor its marketing affiliates shall be
responsible for the use of this information, or of any product, method,
or apparatus mentioned, and you must make your own determination of its
suitability and completeness for your own use, for the protection of the
environment, and for the health and safety of your employees and purchasers
of your products. No warranty is made of the merchantability of fitness
of any product, and nothing herein waives any of the Seller's conditions of sale. |
||
| 3/30/00 10:56:02 AM | ||